Likoloi tsa Motlakase Li-ion Battery Double Side Shiny Copper Foil
Mekhabiso ea koporo e nang le mahlakore a mabeli e bentšitsoeng ka mahlakoreng a mabeli e khetholloa ka sebopeho se lekanang sa mahlakoreng a mabeli, tšepe ea tšepe e haufi le ho teteka ha koporo, boemo bo tlaase haholo ba bokaholimo, bolelele bo babatsehang le matla a tsitsitseng, joalo-joalo.Joalo ka pokello ea li-cathode tsa libeteri tsa lithium, e na le khanyetso e matla ea serame / mocheso mme e ka lelefatsa bophelo ba betri haholo.E ka sebelisoa ka ho pharaletseng ka libeteri bakeng sa likoloi tse ncha tsa matla, indasteri ea 3C e emeloang ke lifono tse bohlale, lik'homphieutha tsa libuka, le tsamaiso ea polokelo ea ESS, le sebaka.
● Botenya: 4.5um 5um 6um 8um 9um 10um 12um
● Bophara: e ka ba ho itšeha joalo ka kopo ea boholo.
● Sephutheloana sa lebokose la lehong, Sephutheloana se ka Hare: se ka fana ka sephutheloana sa Vacuum ha ho hlokahala
● ID: 76 mm, 152 mm
● Bolelele: E hlophisitsoe
● Sample e ka fumaneha
● Bolelele ba Roll / Kantle bophara / bophara ba ka hare: joalo ka kopo
● Bolelele ba mantlha: joalo ka kopo
● Lintho tse ka sehloohong: Pampiri le polasetiki ea ABS & Customize
●Glossy mahlakoreng ka bobeli a phahameng rupture mamello
●Thepa e tsitsitseng e loketseng betri e khonang ho tjhajwa
●Lihlahisoa le lits'ebetso tsa eco-friendly
●Ho tšoana ho babatsehang
●Kenyeletso e ntle haholo
●Likoloi tsa Motlakase
●Li-ion Battery (LiB)
●PC ea Notebook
●Lekolulo
●Capacitor
Karolelano | Yuniti | Tlhokahalo | Mokhoa oa Teko | |||||
Botenya ba lebitso | Um | 6 | 8 | 9 | 10 | 12 | IPC-4562A | |
Boima ba Sebaka | g/m² | 54±2 | 70-75 | 85-90 | 95-100 | 105-110 | IPC-TM-650 2.2.12.2 | |
Bohloeki | % | ≥99.9 | IPC-TM-650 2.3.15 | |||||
makgwakgwa | Lehlakore le benyang (Ra) | սm | ≤0.43 | ≤0.43 | ≤0.43 | ≤0.43 | ≤0.43 | IPC-TM-650 2.3.17 |
Lehlakore la matte(Rz) | um | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | ||
Matla a tšepe | RT(23°C) | Mpa | ≥294 | ≥294 | ≥294 | ≥294 | ≥294 | IPC-TM-650 2.4.18 |
HT(180°C) | ≥196 | ≥196 | ≥196 | ≥196 | ≥196 | |||
Elongation | RT(23°C) | % | ≥5 | ≥5 | ≥5 | ≥5 | ≥5 | IPC-TM-650 2.4.18 |
HT(180°C) | ≥3 | ≥3 | ≥3 | ≥3 | ≥3 | |||
Li-pinholes le porosity | Nomoro | No | IPC-TM-650 2.1.2 | |||||
Mohanyetsi-oxidization | RT(23°C) |
| 90 |
| ||||
RT(160°C) |
| 15 |
|